While investigating a roll forming operation, you initially need to ensure the move structure tooling is composed and manufactured legitimately and will deliver a quality item when every one of the conditions is right. On the off chance that the dividing so as to tool is fine, you have to start the procedure into three territories

  • The roll form machine
  • The material being roll formed
  • The setup of the roll form tooling
  • Then start eliminating the areas as potential causes of the problem.

One of the most neglected areas of a roll forming line is the machine face alignment. It doesn’t matter how well the tooling is built and designed or how good the quality of the steel being roll formed is … if the alignment is bad, the product will be bad.

The First Picture: A quick check with a straight edge on the roll form tooling can indicate a problem with machine face alignment.

Many times a quick check with a straight edge on the tooling can tell you if there is a problem (see the first picture). If you find a problem, you must remove the tooling and align the machine face. The first step in doing a machine face alignment is to check the shafts to make sure they are not loose or have bad bearings. If they are, you’ll need to tighten or fix them like the second picture

The second Picture: First step in doing a machine face alignment is to check the shafts to make sure they are not loose or have bad bearings.

The next step is to remount the outboard stands and set the top shafts parallel to the bottom shafts. This can be done with calipers, a large micrometer, or machine face alignment rolls. When all the top shafts are parallel with the bottom shafts, use a straight edge to align all the bottom shafts to each other, keeping them within 0.005 inch station to station. When all the bottom shafts are aligned to each other, use a smaller straight edge from the bottom shaft to the top shaft to align them to within 0.002 in.

Material Conditions

The condition of the raw material also can affect the quality of the final product. Material thickness variation may occur within the same coil from one end to the other. When it varies from one edge to the other edge, it is called crown. This is a smooth curve of constant variation in thickness.

Usually master mill coils are slit into narrower widths called mults. If the coil has crown, the result of the slitting is two wedge–shaped coils. The one from the center of the master coil will be thicker than the one from the edge of the coil. Volts from a crowned coil also are cambered, which means one coil is longer on the left, while the other is longer on the right. Mill coils with edge wave, then slit into narrow mults, show random camber in the outer strands-first in one direction and then the other. It is impossible to adjust for camber that varies throughout the mults. If the coil has continuous camber in only one direction, twist and sweep will be problems during the roll forming process.

Coil set and cross break may occur if support rolls of the proper configuration are not used at the exit of a material straightened, leveler, or entering feed device. Without the support rolls, the strip breaks harder over the entrance rolls or exit rolls, creating these conditions. Another dimensional variation is crossbow. This condition may occur during the coiling process at the mill or slitter and is caused by an incorrect slitter setup. With crossbow, the top surface of the material, edge to edge, is not equal in length to the bottom surface. The shorter surface is inside of the radius. Forcing material with coil set and crossbow to lie flat will cause oil canning, which means the center of the strip will be longer than the edges. Forcing the material in the opposite direction will cause edge wave.

Tooling Setup

The third area to examine is the tooling setup. You should document setups so they can be repeated as closely as possible each time the tooling is put onto the roll forming machine. One way to do this is to record the flange or hub settings between the rolls with the material in the tooling. Keep the roll form machine and tooling clean and free of any grit or material that may change tooling alignment from top to bottom. Wipe the spacers, shafts, and tooling clean before installation.

The roll form tooling should be producing the desired cross section before the straightened is mounted. If the cross section is not to print, remove the straightener and adjust it before mounting. Roll form tooling that is set up properly will produce a symmetrically shaped part that does not twist

Tricks of the Trade

An optical comparator compares the actual roll form tooling to the original design. Following are some helpful hints that can be used during the troubleshooting of roll form tooling:

  • Use an inspection mirror and flashlight to look for gaps or to see if the roll form tooling is down, touching the material. In these cases, compare the roll design to the actual rolls to ensure they are accurate.
  • Backing up the roll former can allow you to look for pressure marks, misalignment problems in a radius, or roll stops that are being hit too hard.
  • Using a straight edge on the back side of the roll form tooling will indicate machine face alignment problems and will show if the top roll form tooling is parallel with the bottom roll form tooling.
  • If you can’t check the roll tooling with a straight edge, smear grease or heavy oil onto the material and run it through each pass of the roll form tooling. If the grease is heavier on one side of rolls than the other, the top rolls might not be parallel with the bottom rolls
  • If the problem seems to be isolated to one particular pass, cut the material on either side of the pass and raise the roll tooling so that you can remove the material and inspect it for problems.
  • When you can’t isolate the problem, remove the straightener, and then remove one pass at a time. Inspecting the part out of each pass as you remove another will help you isolate the problem.
  • Once you isolate the problem pass, set up the pass in an optical comparator and compare it to the tooling design. It helps if you can enlarge the tooling designs to the magnification of the comparator so an overlay can be done.
  • Wire the problem pass with plug or wire gauges . The gauges can help you check for loose or tight spots.